Copper foil layer pressure plate PZ-22(G)F
We are a productive PZ-22(G)F glazed board, a new type of expansion material for gypsum, Japanese flame retardant environment, resin, product heat resistance, flame retardancy, curl degree, water absorption and hole performance, CTI index etc. National standard requirement, concurrent acquisition CQC product certification; Environmental standard code European Union RoHS, REACH directive requirement. Established in 2006, is now a designated enterprise in China, and has been designated as a "electrical device collection". The most common situation in the market in front of the plate material, the current usage of the electric furnace, microwave furnace, lighting equipment, electronic equipment, furniture table, power supply and other areas.
Features
●优异的冲孔性。最佳冲孔温度为45-70℃
Excellent punching property,Suitable for punching at 45-70℃
<!--[if !supportLists]-->● <!--[endif]-->符合IPC-4101C/10的规范要求
IPC-4101C/10 specification is applicable
General Properties
|
测试项目 Test Item |
单位 Unit |
测试方法 Test Method (IPC-TM-650) |
处理条件 Test Condition |
规范值 Specification (IPC-4101C) |
典型值 Typical Value |
|
铜箔剥离强度 Peel Strength(1oz.) |
N/mm |
2.4.8 |
125℃ |
AABUS |
1.75 |
|
Float260℃/10s |
AABUS |
1.70 |
|||
|
热应力 Thermal Stress |
Sec |
2.4.13.1 |
Float260℃/10s |
≥10 |
20 |
|
弯弓度/翘曲度 Bow/Twist |
% |
2.4.22.1 |
A |
≤1.5 |
0.4/0.55 |
|
抗弯强度 Flexural Strength |
N/mm２ |
2.4.4 |
Warp |
≥242 |
300 |
|
Fill |
≥172 |
240 |
|||
|
燃烧性 Flammability |
Rating |
UL94 |
UL94 |
UL94 V-1 |
V-1 |
|
表面电阻 Surface Resistivity |
MΩ |
2.5.17.1 |
C-96/35/90 |
≥1.0×104 |
1.0×106 |
|
体积电阻 Volume Resistivity |
MΩ－cm |
2.5.17.1 |
C-96/35/90 |
≥1.0×106 |
1.0×108 |
|
介电常数 Dielectric Constant |
― |
2.5.5.2 |
Etched/@1 MHZ |
≤5.4 |
4.5 |
|
介质损耗 Loss Tangent |
― |
2.5.5.2 |
Etched/@1 MHZ |
≤0.035 |
0.02 |
|
耐电弧性 Arc Resistance |
Sec |
2.5.1 |
D-48/50+D-0.5/23 |
≥60 |
120 |
|
吸水率 Moisture Absorption |
% |
2.6.2.1 |
D-24/23 |
≤0.5 |
0.28 |
|
相比漏电起痕指数 Comparative Tranking Index |
V |
IEC60112 |
Etched/0.1%NH4CL |
≥175 |
175 |
Remarks:Typical values for reference only注：典型值制作参考 Specimen Thickness:1.5mm 1/0
A = Keep the specimen originally without any process 保持原样,不作处理
C = Temperature and humidity conditioning 在恒温恒湿的空气中处理
D = Immersing in distilled water with temperature control 浸在恒温的水中处理
E = Temperature conditioning 在恒温的空气中处理